Microstructure Characteristics and Mechanical Properties of Grey Cast Iron at Varied Ferrosilicon Addition
Article Sidebar
Main Article Content
Abstract
Inoculation is an essential metallurgical route for controlling solidification conditions of cast iron, consequently, in this study, the influence of varied percent ferrosilicon (FeSi) addition on microstructure and mechanical properties of grey cast iron (GCI) was investigated. A 50Kg capacity rotary furnace was used to melt the charge (Auto engine block scrap, graphite, ferrosilicon (FeSi) and limestone). The casting was produced in a greensand mold with wooden rectangular pattern of length 50 mm and breadth 30 mm. Chemical compositions and carbon equivalent values (CEVs) of the samples were determined, using Optical emission spectrometry (AR 4 metal analyzer) and the expression respectively. Microstructures of the samples were obtained, using metallurgical microscope (model number NJF-120A). The tensile and hardness properties were measured, using Universal tensile tester and Rockwell hardness tester respectively. From the results, C and Si were the major elements. Other trace elements were Mn, P, S and Al. CEVs of both the control and inoculated samples were less than 4.3%. Microstructure of the control sample was comprised of primary dendrites and graphite flakes, while those of the inoculated samples were characterized by varied amount of more developed primary dendrites, longer graphite flakes and austenite dendrites. Also, a number of small MnS particles were observed in relative amount within the microstructures. Tensile and hardness properties of the FeSi inoculated samples were superior to the control sample. Highest tensile strength and hardness values of 76.62 MPa and 99.89 HRB respectively were obtained at the optimum inoculation of 1.5 wt. % FeSi.
Article Details
This work is licensed under a Creative Commons Attribution-NonCommercial-ShareAlike 4.0 International License.
References
[2] Krause, D. E. (1969). Gray Iron- A Unique Engineering Material. Gray, Ductile and Malleable Iron Castings – Current Capabilities, ASTM STP 455, American Society for Testing and Materials, Philadelphia, 3-28.
[3] Pevec, M., Grega, O., Potrc, I. & Sraml, M. (2014). Elevated Temperature Low Cycle Fatigue of Grey Cast Iron Used For Automotive Brake Discs. Engineering Failure Analysis, 42(1), 221-230
[4] Hsu, C. H. & Lin, K .T. (2011). A Study on Microstructure and Toughness of Copper Alloyed and Austempered Ductile Irons. Materials science and engineering A. 183–187
[5] Davis, J. R. (1996). Classification and basic metallurgy of cast irons. American Society of Metal (ASM), Specialty Handbook Cast Irons, 10-20.
[6] Collini, L., Nicoletto G. & Konecna, R. (2008). Microstructure and Mechanical Properties of Pearlitic Gray Cast Iron. Mater. Sci. Eng. A.488, 529–539.
[7] Behnam, M.M.J., Davami, P & Varahram, N. (2010). Effect of Cooling Rate on Microstructure and Mechanical Properties of Grey Cast Iron. Materials Science and Engineering, A528, (2), 583–588.
[8] Chisamera, M., Riposan I., Stan S., Militaru C., Anton I. & Barstow M. (2012). Inoculated Slightly Hypereutectic Gray Cast Irons. J. Mater. Eng. Perform. 331–338.
[9] Harvey, J. N. & Noble, G.A. (2007). Inoculation of Cast Irons- An Overview- Tennant Metallurgical Group Ltd, Hesterfield, United Kingdom, 55th Indian Foundry Congress 2007.
[10] Edalati, K., Akhlaghi F. & Nih-Ahmadabadi A. (2005). Influence of SiC and FeSi Addition on the Characteristics of Gray Cast Iron Melts Poured at Different Temperatures. J. Mater. Process. Technol., 160, 261-265.
[11] John, R. B. (2010). Foseco Ferrous Foundryman’s Handbook, A division of Reed Educational and Professional Publishing Ltd.. Oxford Auckland Boston Johannesburg Melbourne New Delhi, Butterworth-Heinemann, Linacre House, Jordan Hill, Oxford OX2 8DP 225Wildwood Avenue, Woburn, MA 01801-2041, 62-66.
[12] Khanna, O.P. (2002). A Textbook of Foundry Technology, 9th ed., Dhampart Rai Publications, New Delhi
[13] Soiński, M. S., & Wawrzyniec A. (2010). Initial assessment of effectiveness of some selected inoculants for grey cast iron, Chair of Foundry, Technical University of Częstochowa, av. Armii Krajowej 19, Częstochowa, Poland.. 27.
[14] Stan, S., Chisamera, M. & Riposan I. (2009). Solidification Pattern of Hypoeutectic Grey Cast Iron in Wedge Test Samples POLITEHNICA University of Bucharest, Romania, Metallurgical International. XIV (2)
[15] Fras, E. & Gorny, M. (2012). Inoculation Effects of Cast Iron, Archives of Foundry Engineering, 12(4), 34-46.
[16] Dhruv P, Nanavati P. K & Chug C. M. (2013). Effect of Ca and Ba containing Ferrosilicon Inoculants on Microstructure and Tensile Properties of IS-210, and IS-1862 Cast Irons. National Conference on Engineering trends in Engineering Technology and Management, Ahmedabad, Gujarat.
[17] Fengzhang, R.E.N, Fengju Li, Weiming L.I.U, Zhanhang, M.A & Baohong, T. (2009). Effect of Inoculation Addition on Machinability of Grey Cast Iron, Journal of Rare Earths, 27(2), 294-299.
[18] Hirs, A., Glavas., Z. & Straly, A. (2022). Effect of Inoculation, Cooling Rate and Change Composition on Grey Cast Iron Microstructures, International Journal of Material Science, 1, 3-6.
[19] Diego, R., Joao, R., Sartori., M. & Andre. A. V. (2015). Effect of Different Inoculant on Microstructural Characteristics of Grey Cast Iron GG-25, Hardness and Useful Life Tool, Acta Scientiarum, 37(4), .355-360. doi:http://dx.doi.org/10.1016/j.engfailanal.2014.03.021
[20] Izudin, D. & Ingvar, L. S., (1998). The effect of inoculant amount and casting temperature on metal expansion penetration in grey cast iron. The Sixth International Symposium on Casting, Alabama, Paper 59.
[21] Szczesny, S., Kopycinski, D. & Guzik, E. (2020). Inoculation of Grey Cast Iron Intended For Large Scale and Heavy Weight Castings of Bottom Plates and Counterweights Manufactured in the Krakodlew S.A. Archives of Foundry Engineering, 22(1), 19-24.
[22] Reyes-Castellanos, G., Crux-Ramirez, A., Hygo-Guitierrez-Perez, V., Rivera-Salinas, J. E., Sanchez-Alvardo, R.G. & Cohn-Garcia, E .(2021). Experimental Assessment of The Grey Cast Iron Production by Inoculant Injection, Journal of Mining and Metallurgy, 57(1), 41-51.
[23] Saliu, O. S., Henry, K. T. & Akande, A. S. (2018). Effect of Inoculation on Varying Wall Thickness in Gray Cast Iron. ACTA TECHNICA CORVINIENSIS- Bulletin of Engineering.
[24] Borse S. C. & Manguther, Y.E. (2014). Review on Grey Cast Iron, International Journal of Innovative Research in Science, Engineering and Technology, 3(4), 29-36.
[25] Guiquan, W., Xiang, C., Yangxiang, L. & Zhangli, L. (2018). Effect of Inoculation on the Pearlitic Grey Cast Iron With High Thermal Conductivity and Tensile Strength, Materials, 11(10), 187.
[26] Collin, L., Nicoletto, G. & Konecna, R. (2008). Microstructure and Mechanical Properties of Pearlite Grey Cast Iron, Material Science and Engineering A,v. 488, (1-2), 529-539.
[27] American Standard for testing and measurement (ASTM) E3-11 (2011). Standard Guide for Preparation of Metallographic Specimens, ASTM International, West Conshohocken, www.astm.org
[28] American Standard For Testing and Measurement (ASTM) E8-04. (2008). Standard Test Methods for Tension Testing of Metallic Materials, ASTM International, West Conshohocken, www.astm.org
[29] American Standard for Testing and Measurement (ASTM) E384-11 (2011). Standard Test Method for Microindentation Hardness of Materials, ASTM International. West Conshohocken, www.astm.org\
[30] Sahu, S., Bhat, M.N., Kumar, A., Pratik, A & Kumar A. (2014). Effect Of Section Thickness On The Microstructure And Hardness Of Grey Cast Iron (A Simulation Study).International Journal of Engineering Research and Technology, 3(7), 35- 40.
[31] Pluphrach, G. (2010). Study of the Effect of Solidification on Graphite Flakes Microstructure and Mechanical Properties of An ASTM A-48 Grey Cast Iron Using Steel Molds. Songklanakarin Journal of Science andTechnology, 32(6), 613-618.
[32] Adedayo, A.V. (2013). Relationship between Graphite Flake Sizes and the Mechanical Properties of Grey iron. International Journal of Materials Science and Application, 2(3), 94-98.